"Vapochromic" Compounds as Environmental Sensors. 2. Synthesis and Near-Infrared and Infrared Spectroscopy Studies of [Pt(arylisocyanide)4][Pt(CN)4] upon Exposure to Volatile Organic Compound Vapors

Charles A. Daws, Chris Exstrom, John R. Sowa, Kent R. Mann

Research output: Contribution to journalArticle

161 Citations (Scopus)

Abstract

The synthesis, characterization, and vis-NIR-IR vapochromic/spectroscopic studies are reported for isocyanide compounds of the form [Pt(arylisocyanide)4][Pt(CN)4] (where arylisocyanide =p-CNC6H4CnH2n+1; n = 1, 6, 10, 12, 14). The dark blue, solid materials change color in the NIR (near-infrared) spectral region upon exposure to the ambient room-temperature vapor pressure of volatile organic compounds (VOCs). At room temperature the PtPt compounds exhibit strong solid-state absorption and emission bands in the NIR region of the spectrum that are red-shifted from similar bands in the PtPd analogues; (n = 1, γmax abs = 744, γmax emit = 958; n = 6, γmax abs = 841, γmax emit = 910; n = 10, γmax abs = 746, γmax emit = 944; n = 12, γmax abs = 764, γmax emit = 912; n = 14, γmax abs = 690, γmax emit = 876 nm). The positions of these broad bands depend on the number of carbons in the alkyl substituent. The absorption and emission bands for the solid material (n = 10 compound) also exhibit a substantial red-shift upon cooling to 77 K (γmax abs (293 K) = 746; γmax emit (293 K) = 944; γmax abs (77 K) = 846; γmax emit (77 K) = 1094 nm) that is consistent with an alternating cation-anion stacked structure. Qualitatively, compounds with n > 6 respond well to nonpolar VOCs; the n = 1, 6 compounds respond better to polar VOCs. The shifts observed for γmax abs (at 293 K) are on the order of 700 cm-1 and are 2-3 times greater than those exhibited by the PtPd analogue compounds under identical conditions. The n = 10 compound is the most responsive; the positions of the vis - NIR band in the presence of several solvent vapors are as follows: none, 746 nm; methanol, 757; ethanol, 782; 2-propanol, 782; diethyl ether, 787; acetonitrile, 809; hexanes, 775; acetone, 800; benzene, 801; dichloromethane, 811; chloroform, 837. No response was observed for water vapor. IR studies of films of the n = 10 compound on an ATR crystal show that the sorption of VOC by the solid causes no change in the v(CN) isocyanide stretching frequency but in some cases a substantial shift (0-15 cm-1) in v(CN) of the cyanide stretch is observed. When the n = 10 compound contacts VOCs capable of H-bonding with the Pt(CN)42-anion, two cyanide stretches are observed. All the spectroscopic data suggest that the VOC penetrates the solid and interacts with the linear chain chromophore to cause the spectral shifts in the vis-NIR-IR spectral regions. The vapochromic shifts are suggested to be due to dipole-dipole and/or H-bonding interactions between the Pt(CN)42- anion and polar VOCs. For nonpolar VOCs, lypophilic interactions between the VOC and the isocyanide ligands that cause no change in the v-(CN) stretching region must cause the NIR vapochromism observed. The absence of a vapochromic response for water vapor is suggested to arise from hydrophobic blocking of the water at the solid/gas interface.

Original languageEnglish (US)
Pages (from-to)363-368
Number of pages6
JournalChemistry of Materials
Volume9
Issue number1
StatePublished - Jan 1 1997

Fingerprint

Volatile Organic Compounds
Volatile organic compounds
Infrared spectroscopy
Vapors
Infrared radiation
Cyanides
Sensors
Anions
Negative ions
Steam
Water vapor
Stretching
2-Propanol
Methylene Chloride
Dichloromethane
Hexanes
Propanol
Chromophores
Chloroform
Chlorine compounds

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)
  • Materials Chemistry

Cite this

@article{ae0a20c1fa474586a9908895420de23a,
title = "{"}Vapochromic{"} Compounds as Environmental Sensors. 2. Synthesis and Near-Infrared and Infrared Spectroscopy Studies of [Pt(arylisocyanide)4][Pt(CN)4] upon Exposure to Volatile Organic Compound Vapors",
abstract = "The synthesis, characterization, and vis-NIR-IR vapochromic/spectroscopic studies are reported for isocyanide compounds of the form [Pt(arylisocyanide)4][Pt(CN)4] (where arylisocyanide =p-CNC6H4CnH2n+1; n = 1, 6, 10, 12, 14). The dark blue, solid materials change color in the NIR (near-infrared) spectral region upon exposure to the ambient room-temperature vapor pressure of volatile organic compounds (VOCs). At room temperature the PtPt compounds exhibit strong solid-state absorption and emission bands in the NIR region of the spectrum that are red-shifted from similar bands in the PtPd analogues; (n = 1, γmax abs = 744, γmax emit = 958; n = 6, γmax abs = 841, γmax emit = 910; n = 10, γmax abs = 746, γmax emit = 944; n = 12, γmax abs = 764, γmax emit = 912; n = 14, γmax abs = 690, γmax emit = 876 nm). The positions of these broad bands depend on the number of carbons in the alkyl substituent. The absorption and emission bands for the solid material (n = 10 compound) also exhibit a substantial red-shift upon cooling to 77 K (γmax abs (293 K) = 746; γmax emit (293 K) = 944; γmax abs (77 K) = 846; γmax emit (77 K) = 1094 nm) that is consistent with an alternating cation-anion stacked structure. Qualitatively, compounds with n > 6 respond well to nonpolar VOCs; the n = 1, 6 compounds respond better to polar VOCs. The shifts observed for γmax abs (at 293 K) are on the order of 700 cm-1 and are 2-3 times greater than those exhibited by the PtPd analogue compounds under identical conditions. The n = 10 compound is the most responsive; the positions of the vis - NIR band in the presence of several solvent vapors are as follows: none, 746 nm; methanol, 757; ethanol, 782; 2-propanol, 782; diethyl ether, 787; acetonitrile, 809; hexanes, 775; acetone, 800; benzene, 801; dichloromethane, 811; chloroform, 837. No response was observed for water vapor. IR studies of films of the n = 10 compound on an ATR crystal show that the sorption of VOC by the solid causes no change in the v(CN) isocyanide stretching frequency but in some cases a substantial shift (0-15 cm-1) in v(CN) of the cyanide stretch is observed. When the n = 10 compound contacts VOCs capable of H-bonding with the Pt(CN)42-anion, two cyanide stretches are observed. All the spectroscopic data suggest that the VOC penetrates the solid and interacts with the linear chain chromophore to cause the spectral shifts in the vis-NIR-IR spectral regions. The vapochromic shifts are suggested to be due to dipole-dipole and/or H-bonding interactions between the Pt(CN)42- anion and polar VOCs. For nonpolar VOCs, lypophilic interactions between the VOC and the isocyanide ligands that cause no change in the v-(CN) stretching region must cause the NIR vapochromism observed. The absence of a vapochromic response for water vapor is suggested to arise from hydrophobic blocking of the water at the solid/gas interface.",
author = "Daws, {Charles A.} and Chris Exstrom and Sowa, {John R.} and Mann, {Kent R.}",
year = "1997",
month = "1",
day = "1",
language = "English (US)",
volume = "9",
pages = "363--368",
journal = "Chemistry of Materials",
issn = "0897-4756",
publisher = "American Chemical Society",
number = "1",

}

TY - JOUR

T1 - "Vapochromic" Compounds as Environmental Sensors. 2. Synthesis and Near-Infrared and Infrared Spectroscopy Studies of [Pt(arylisocyanide)4][Pt(CN)4] upon Exposure to Volatile Organic Compound Vapors

AU - Daws, Charles A.

AU - Exstrom, Chris

AU - Sowa, John R.

AU - Mann, Kent R.

PY - 1997/1/1

Y1 - 1997/1/1

N2 - The synthesis, characterization, and vis-NIR-IR vapochromic/spectroscopic studies are reported for isocyanide compounds of the form [Pt(arylisocyanide)4][Pt(CN)4] (where arylisocyanide =p-CNC6H4CnH2n+1; n = 1, 6, 10, 12, 14). The dark blue, solid materials change color in the NIR (near-infrared) spectral region upon exposure to the ambient room-temperature vapor pressure of volatile organic compounds (VOCs). At room temperature the PtPt compounds exhibit strong solid-state absorption and emission bands in the NIR region of the spectrum that are red-shifted from similar bands in the PtPd analogues; (n = 1, γmax abs = 744, γmax emit = 958; n = 6, γmax abs = 841, γmax emit = 910; n = 10, γmax abs = 746, γmax emit = 944; n = 12, γmax abs = 764, γmax emit = 912; n = 14, γmax abs = 690, γmax emit = 876 nm). The positions of these broad bands depend on the number of carbons in the alkyl substituent. The absorption and emission bands for the solid material (n = 10 compound) also exhibit a substantial red-shift upon cooling to 77 K (γmax abs (293 K) = 746; γmax emit (293 K) = 944; γmax abs (77 K) = 846; γmax emit (77 K) = 1094 nm) that is consistent with an alternating cation-anion stacked structure. Qualitatively, compounds with n > 6 respond well to nonpolar VOCs; the n = 1, 6 compounds respond better to polar VOCs. The shifts observed for γmax abs (at 293 K) are on the order of 700 cm-1 and are 2-3 times greater than those exhibited by the PtPd analogue compounds under identical conditions. The n = 10 compound is the most responsive; the positions of the vis - NIR band in the presence of several solvent vapors are as follows: none, 746 nm; methanol, 757; ethanol, 782; 2-propanol, 782; diethyl ether, 787; acetonitrile, 809; hexanes, 775; acetone, 800; benzene, 801; dichloromethane, 811; chloroform, 837. No response was observed for water vapor. IR studies of films of the n = 10 compound on an ATR crystal show that the sorption of VOC by the solid causes no change in the v(CN) isocyanide stretching frequency but in some cases a substantial shift (0-15 cm-1) in v(CN) of the cyanide stretch is observed. When the n = 10 compound contacts VOCs capable of H-bonding with the Pt(CN)42-anion, two cyanide stretches are observed. All the spectroscopic data suggest that the VOC penetrates the solid and interacts with the linear chain chromophore to cause the spectral shifts in the vis-NIR-IR spectral regions. The vapochromic shifts are suggested to be due to dipole-dipole and/or H-bonding interactions between the Pt(CN)42- anion and polar VOCs. For nonpolar VOCs, lypophilic interactions between the VOC and the isocyanide ligands that cause no change in the v-(CN) stretching region must cause the NIR vapochromism observed. The absence of a vapochromic response for water vapor is suggested to arise from hydrophobic blocking of the water at the solid/gas interface.

AB - The synthesis, characterization, and vis-NIR-IR vapochromic/spectroscopic studies are reported for isocyanide compounds of the form [Pt(arylisocyanide)4][Pt(CN)4] (where arylisocyanide =p-CNC6H4CnH2n+1; n = 1, 6, 10, 12, 14). The dark blue, solid materials change color in the NIR (near-infrared) spectral region upon exposure to the ambient room-temperature vapor pressure of volatile organic compounds (VOCs). At room temperature the PtPt compounds exhibit strong solid-state absorption and emission bands in the NIR region of the spectrum that are red-shifted from similar bands in the PtPd analogues; (n = 1, γmax abs = 744, γmax emit = 958; n = 6, γmax abs = 841, γmax emit = 910; n = 10, γmax abs = 746, γmax emit = 944; n = 12, γmax abs = 764, γmax emit = 912; n = 14, γmax abs = 690, γmax emit = 876 nm). The positions of these broad bands depend on the number of carbons in the alkyl substituent. The absorption and emission bands for the solid material (n = 10 compound) also exhibit a substantial red-shift upon cooling to 77 K (γmax abs (293 K) = 746; γmax emit (293 K) = 944; γmax abs (77 K) = 846; γmax emit (77 K) = 1094 nm) that is consistent with an alternating cation-anion stacked structure. Qualitatively, compounds with n > 6 respond well to nonpolar VOCs; the n = 1, 6 compounds respond better to polar VOCs. The shifts observed for γmax abs (at 293 K) are on the order of 700 cm-1 and are 2-3 times greater than those exhibited by the PtPd analogue compounds under identical conditions. The n = 10 compound is the most responsive; the positions of the vis - NIR band in the presence of several solvent vapors are as follows: none, 746 nm; methanol, 757; ethanol, 782; 2-propanol, 782; diethyl ether, 787; acetonitrile, 809; hexanes, 775; acetone, 800; benzene, 801; dichloromethane, 811; chloroform, 837. No response was observed for water vapor. IR studies of films of the n = 10 compound on an ATR crystal show that the sorption of VOC by the solid causes no change in the v(CN) isocyanide stretching frequency but in some cases a substantial shift (0-15 cm-1) in v(CN) of the cyanide stretch is observed. When the n = 10 compound contacts VOCs capable of H-bonding with the Pt(CN)42-anion, two cyanide stretches are observed. All the spectroscopic data suggest that the VOC penetrates the solid and interacts with the linear chain chromophore to cause the spectral shifts in the vis-NIR-IR spectral regions. The vapochromic shifts are suggested to be due to dipole-dipole and/or H-bonding interactions between the Pt(CN)42- anion and polar VOCs. For nonpolar VOCs, lypophilic interactions between the VOC and the isocyanide ligands that cause no change in the v-(CN) stretching region must cause the NIR vapochromism observed. The absence of a vapochromic response for water vapor is suggested to arise from hydrophobic blocking of the water at the solid/gas interface.

UR - http://www.scopus.com/inward/record.url?scp=0001588390&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0001588390&partnerID=8YFLogxK

M3 - Article

VL - 9

SP - 363

EP - 368

JO - Chemistry of Materials

JF - Chemistry of Materials

SN - 0897-4756

IS - 1

ER -