Unraveling the Complex Hydration Behavior of Ionomers under Thin Film Confinement

Shudipto K. Dishari, Christopher A. Rumble, Mark Maroncelli, Joseph A. Dura, Michael A. Hickner

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

The mechanical and transport properties of submicron thick ionomer films are crucial in the study and understanding of the ionomer-catalyst interfaces in the porous electrodes of energy conversion and storage devices, such as fuel cells and batteries. Interestingly, ionomers in thin films behave differently from bulk ionomer membranes, and the behavior of these thin films is not well understood. The complex hydration behavior of thin ionomer films in the confined state is described in this work. Here, thin films (∼25-250 nm) of sulfonated Radel (S-Radel) were investigated to understand thickness and hydration effects on the density and mechanical properties of these sulfonated thin polymer films. The density values obtained from quartz crystal microbalance and spectroscopic ellipsometry showed a thickness trend similar to density values obtained from neutron reflectometry with thin films of ∼25 nm thickness having lower densities than thicker, ∼250 nm films. Thicker films were always more dense and less water-rich at the interface compared to thinner samples. The mechanical properties of nanoscale thick polymer films are challenging to probe with traditional techniques. A fluorescent rotor probe was thus incorporated into the polymer samples to infer the distribution of material stiffness from fluorescence lifetime measurements. The lower density of the thin films as measured by ellipsometry and neutron reflectometry rationalized greater mobility from fluorescence measurements in the thinner films when dry. When the thin sample was hydrated, the film density and interfacial water volume fraction significantly increased. Also, the samples with lower thicknesses antiplasticized, indicating poor water-polymer mobility inside the film. The plasticization properties and water-polymer mobility appeared to be controlled by both film density and competing interfacial phenomena, between the air-polymer and polymer-substrate interfaces, depending on the level of hydration.

Original languageEnglish (US)
Pages (from-to)3471-3481
Number of pages11
JournalJournal of Physical Chemistry C
Volume122
Issue number6
DOIs
StatePublished - Feb 15 2018

Fingerprint

Ionomers
Hydration
hydration
Thin films
Polymers
polymers
thin films
Water
mechanical properties
Polymer films
Thick films
Mechanical properties
water
ellipsometry
thick films
Fuel cells
Neutrons
Fluorescence
neutrons
fluorescence

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Energy(all)
  • Physical and Theoretical Chemistry
  • Surfaces, Coatings and Films

Cite this

Unraveling the Complex Hydration Behavior of Ionomers under Thin Film Confinement. / Dishari, Shudipto K.; Rumble, Christopher A.; Maroncelli, Mark; Dura, Joseph A.; Hickner, Michael A.

In: Journal of Physical Chemistry C, Vol. 122, No. 6, 15.02.2018, p. 3471-3481.

Research output: Contribution to journalArticle

Dishari, Shudipto K. ; Rumble, Christopher A. ; Maroncelli, Mark ; Dura, Joseph A. ; Hickner, Michael A. / Unraveling the Complex Hydration Behavior of Ionomers under Thin Film Confinement. In: Journal of Physical Chemistry C. 2018 ; Vol. 122, No. 6. pp. 3471-3481.
@article{1659609b6e174e068f3b076a8400f8ba,
title = "Unraveling the Complex Hydration Behavior of Ionomers under Thin Film Confinement",
abstract = "The mechanical and transport properties of submicron thick ionomer films are crucial in the study and understanding of the ionomer-catalyst interfaces in the porous electrodes of energy conversion and storage devices, such as fuel cells and batteries. Interestingly, ionomers in thin films behave differently from bulk ionomer membranes, and the behavior of these thin films is not well understood. The complex hydration behavior of thin ionomer films in the confined state is described in this work. Here, thin films (∼25-250 nm) of sulfonated Radel (S-Radel) were investigated to understand thickness and hydration effects on the density and mechanical properties of these sulfonated thin polymer films. The density values obtained from quartz crystal microbalance and spectroscopic ellipsometry showed a thickness trend similar to density values obtained from neutron reflectometry with thin films of ∼25 nm thickness having lower densities than thicker, ∼250 nm films. Thicker films were always more dense and less water-rich at the interface compared to thinner samples. The mechanical properties of nanoscale thick polymer films are challenging to probe with traditional techniques. A fluorescent rotor probe was thus incorporated into the polymer samples to infer the distribution of material stiffness from fluorescence lifetime measurements. The lower density of the thin films as measured by ellipsometry and neutron reflectometry rationalized greater mobility from fluorescence measurements in the thinner films when dry. When the thin sample was hydrated, the film density and interfacial water volume fraction significantly increased. Also, the samples with lower thicknesses antiplasticized, indicating poor water-polymer mobility inside the film. The plasticization properties and water-polymer mobility appeared to be controlled by both film density and competing interfacial phenomena, between the air-polymer and polymer-substrate interfaces, depending on the level of hydration.",
author = "Dishari, {Shudipto K.} and Rumble, {Christopher A.} and Mark Maroncelli and Dura, {Joseph A.} and Hickner, {Michael A.}",
year = "2018",
month = "2",
day = "15",
doi = "10.1021/acs.jpcc.7b11888",
language = "English (US)",
volume = "122",
pages = "3471--3481",
journal = "Journal of Physical Chemistry C",
issn = "1932-7447",
publisher = "American Chemical Society",
number = "6",

}

TY - JOUR

T1 - Unraveling the Complex Hydration Behavior of Ionomers under Thin Film Confinement

AU - Dishari, Shudipto K.

AU - Rumble, Christopher A.

AU - Maroncelli, Mark

AU - Dura, Joseph A.

AU - Hickner, Michael A.

PY - 2018/2/15

Y1 - 2018/2/15

N2 - The mechanical and transport properties of submicron thick ionomer films are crucial in the study and understanding of the ionomer-catalyst interfaces in the porous electrodes of energy conversion and storage devices, such as fuel cells and batteries. Interestingly, ionomers in thin films behave differently from bulk ionomer membranes, and the behavior of these thin films is not well understood. The complex hydration behavior of thin ionomer films in the confined state is described in this work. Here, thin films (∼25-250 nm) of sulfonated Radel (S-Radel) were investigated to understand thickness and hydration effects on the density and mechanical properties of these sulfonated thin polymer films. The density values obtained from quartz crystal microbalance and spectroscopic ellipsometry showed a thickness trend similar to density values obtained from neutron reflectometry with thin films of ∼25 nm thickness having lower densities than thicker, ∼250 nm films. Thicker films were always more dense and less water-rich at the interface compared to thinner samples. The mechanical properties of nanoscale thick polymer films are challenging to probe with traditional techniques. A fluorescent rotor probe was thus incorporated into the polymer samples to infer the distribution of material stiffness from fluorescence lifetime measurements. The lower density of the thin films as measured by ellipsometry and neutron reflectometry rationalized greater mobility from fluorescence measurements in the thinner films when dry. When the thin sample was hydrated, the film density and interfacial water volume fraction significantly increased. Also, the samples with lower thicknesses antiplasticized, indicating poor water-polymer mobility inside the film. The plasticization properties and water-polymer mobility appeared to be controlled by both film density and competing interfacial phenomena, between the air-polymer and polymer-substrate interfaces, depending on the level of hydration.

AB - The mechanical and transport properties of submicron thick ionomer films are crucial in the study and understanding of the ionomer-catalyst interfaces in the porous electrodes of energy conversion and storage devices, such as fuel cells and batteries. Interestingly, ionomers in thin films behave differently from bulk ionomer membranes, and the behavior of these thin films is not well understood. The complex hydration behavior of thin ionomer films in the confined state is described in this work. Here, thin films (∼25-250 nm) of sulfonated Radel (S-Radel) were investigated to understand thickness and hydration effects on the density and mechanical properties of these sulfonated thin polymer films. The density values obtained from quartz crystal microbalance and spectroscopic ellipsometry showed a thickness trend similar to density values obtained from neutron reflectometry with thin films of ∼25 nm thickness having lower densities than thicker, ∼250 nm films. Thicker films were always more dense and less water-rich at the interface compared to thinner samples. The mechanical properties of nanoscale thick polymer films are challenging to probe with traditional techniques. A fluorescent rotor probe was thus incorporated into the polymer samples to infer the distribution of material stiffness from fluorescence lifetime measurements. The lower density of the thin films as measured by ellipsometry and neutron reflectometry rationalized greater mobility from fluorescence measurements in the thinner films when dry. When the thin sample was hydrated, the film density and interfacial water volume fraction significantly increased. Also, the samples with lower thicknesses antiplasticized, indicating poor water-polymer mobility inside the film. The plasticization properties and water-polymer mobility appeared to be controlled by both film density and competing interfacial phenomena, between the air-polymer and polymer-substrate interfaces, depending on the level of hydration.

UR - http://www.scopus.com/inward/record.url?scp=85042157564&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85042157564&partnerID=8YFLogxK

U2 - 10.1021/acs.jpcc.7b11888

DO - 10.1021/acs.jpcc.7b11888

M3 - Article

AN - SCOPUS:85042157564

VL - 122

SP - 3471

EP - 3481

JO - Journal of Physical Chemistry C

JF - Journal of Physical Chemistry C

SN - 1932-7447

IS - 6

ER -