Structure, magnetic properties, and exchange coupling in thermally processed NdDyFeCoB/α-Fe nanoscale multilayer magnets

W. Liu, X. Z. Li, Y. C. Sui, J. Zhou, W. J. Ren, Z. D. Zhang, David J Sellmyer

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

The structure and magnetic properties of multilayer magnets with a hard phase (HP1= Nd13.5 Dy1.5 Fe68 Co10 B7 or HP2= Nd14 Dy1 Fe68 Co10 B7) and soft phase Fe, prepared by sputtering and subsequent heat treatment, have been investigated. For SiTi (20 nm) [HP1 (2.0 nm) Fe (0.5 nm)] ×200Ti (10 nm) multilayer film, transmission electron microscopy results show that Fe disperses in amorphous NdDyFeCoB alloy. After annealing at 575 °C for 5 min, the hard Nd2 Fe14 B phase typically with grains of about 50 nm and some amount of α-Fe coexist in the film. The grain size of the hard and soft phases can be controlled by the proper thickness of the layer and the period. A coercivity of 7.7 kOe and a ratio Mr Ms of 0.74 are achieved in the multilayer SiTi (20 nm) [HP2 (2 nm) Fe (0.5 nm)] ×200Ti (10 nm). A good squareness of the hysteresis loop (measured even at 200 K) is observed, due to the effective exchange coupling between the magnetically soft and hard nanograins in the film. A pinning-type mechanism dominates the magnetization reversal process. In addition, the effect of the effective anisotropy, the grain size, and interfaces between the magnetically hard and soft phases on the exchange coupling is discussed.

Original languageEnglish (US)
Article number07E130
JournalJournal of Applied Physics
Volume103
Issue number7
DOIs
StatePublished - Apr 21 2008

Fingerprint

magnets
magnetic properties
grain size
coercivity
heat treatment
sputtering
hysteresis
magnetization
transmission electron microscopy
anisotropy
annealing

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Structure, magnetic properties, and exchange coupling in thermally processed NdDyFeCoB/α-Fe nanoscale multilayer magnets. / Liu, W.; Li, X. Z.; Sui, Y. C.; Zhou, J.; Ren, W. J.; Zhang, Z. D.; Sellmyer, David J.

In: Journal of Applied Physics, Vol. 103, No. 7, 07E130, 21.04.2008.

Research output: Contribution to journalArticle

@article{8e8868dac3bb42efb85d9b11e364c2e6,
title = "Structure, magnetic properties, and exchange coupling in thermally processed NdDyFeCoB/α-Fe nanoscale multilayer magnets",
abstract = "The structure and magnetic properties of multilayer magnets with a hard phase (HP1= Nd13.5 Dy1.5 Fe68 Co10 B7 or HP2= Nd14 Dy1 Fe68 Co10 B7) and soft phase Fe, prepared by sputtering and subsequent heat treatment, have been investigated. For SiTi (20 nm) [HP1 (2.0 nm) Fe (0.5 nm)] ×200Ti (10 nm) multilayer film, transmission electron microscopy results show that Fe disperses in amorphous NdDyFeCoB alloy. After annealing at 575 °C for 5 min, the hard Nd2 Fe14 B phase typically with grains of about 50 nm and some amount of α-Fe coexist in the film. The grain size of the hard and soft phases can be controlled by the proper thickness of the layer and the period. A coercivity of 7.7 kOe and a ratio Mr Ms of 0.74 are achieved in the multilayer SiTi (20 nm) [HP2 (2 nm) Fe (0.5 nm)] ×200Ti (10 nm). A good squareness of the hysteresis loop (measured even at 200 K) is observed, due to the effective exchange coupling between the magnetically soft and hard nanograins in the film. A pinning-type mechanism dominates the magnetization reversal process. In addition, the effect of the effective anisotropy, the grain size, and interfaces between the magnetically hard and soft phases on the exchange coupling is discussed.",
author = "W. Liu and Li, {X. Z.} and Sui, {Y. C.} and J. Zhou and Ren, {W. J.} and Zhang, {Z. D.} and Sellmyer, {David J}",
year = "2008",
month = "4",
day = "21",
doi = "10.1063/1.2834254",
language = "English (US)",
volume = "103",
journal = "Journal of Applied Physics",
issn = "0021-8979",
publisher = "American Institute of Physics Publising LLC",
number = "7",

}

TY - JOUR

T1 - Structure, magnetic properties, and exchange coupling in thermally processed NdDyFeCoB/α-Fe nanoscale multilayer magnets

AU - Liu, W.

AU - Li, X. Z.

AU - Sui, Y. C.

AU - Zhou, J.

AU - Ren, W. J.

AU - Zhang, Z. D.

AU - Sellmyer, David J

PY - 2008/4/21

Y1 - 2008/4/21

N2 - The structure and magnetic properties of multilayer magnets with a hard phase (HP1= Nd13.5 Dy1.5 Fe68 Co10 B7 or HP2= Nd14 Dy1 Fe68 Co10 B7) and soft phase Fe, prepared by sputtering and subsequent heat treatment, have been investigated. For SiTi (20 nm) [HP1 (2.0 nm) Fe (0.5 nm)] ×200Ti (10 nm) multilayer film, transmission electron microscopy results show that Fe disperses in amorphous NdDyFeCoB alloy. After annealing at 575 °C for 5 min, the hard Nd2 Fe14 B phase typically with grains of about 50 nm and some amount of α-Fe coexist in the film. The grain size of the hard and soft phases can be controlled by the proper thickness of the layer and the period. A coercivity of 7.7 kOe and a ratio Mr Ms of 0.74 are achieved in the multilayer SiTi (20 nm) [HP2 (2 nm) Fe (0.5 nm)] ×200Ti (10 nm). A good squareness of the hysteresis loop (measured even at 200 K) is observed, due to the effective exchange coupling between the magnetically soft and hard nanograins in the film. A pinning-type mechanism dominates the magnetization reversal process. In addition, the effect of the effective anisotropy, the grain size, and interfaces between the magnetically hard and soft phases on the exchange coupling is discussed.

AB - The structure and magnetic properties of multilayer magnets with a hard phase (HP1= Nd13.5 Dy1.5 Fe68 Co10 B7 or HP2= Nd14 Dy1 Fe68 Co10 B7) and soft phase Fe, prepared by sputtering and subsequent heat treatment, have been investigated. For SiTi (20 nm) [HP1 (2.0 nm) Fe (0.5 nm)] ×200Ti (10 nm) multilayer film, transmission electron microscopy results show that Fe disperses in amorphous NdDyFeCoB alloy. After annealing at 575 °C for 5 min, the hard Nd2 Fe14 B phase typically with grains of about 50 nm and some amount of α-Fe coexist in the film. The grain size of the hard and soft phases can be controlled by the proper thickness of the layer and the period. A coercivity of 7.7 kOe and a ratio Mr Ms of 0.74 are achieved in the multilayer SiTi (20 nm) [HP2 (2 nm) Fe (0.5 nm)] ×200Ti (10 nm). A good squareness of the hysteresis loop (measured even at 200 K) is observed, due to the effective exchange coupling between the magnetically soft and hard nanograins in the film. A pinning-type mechanism dominates the magnetization reversal process. In addition, the effect of the effective anisotropy, the grain size, and interfaces between the magnetically hard and soft phases on the exchange coupling is discussed.

UR - http://www.scopus.com/inward/record.url?scp=42149142328&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=42149142328&partnerID=8YFLogxK

U2 - 10.1063/1.2834254

DO - 10.1063/1.2834254

M3 - Article

VL - 103

JO - Journal of Applied Physics

JF - Journal of Applied Physics

SN - 0021-8979

IS - 7

M1 - 07E130

ER -