Raman spectroscopy of phenylcarbyne polymer films under pulsed green laser irradiation

Y. F. Lu, S. M. Huang, Z. Sun

Research output: Contribution to journalArticle

35 Citations (Scopus)

Abstract

The polycarbyne polymer films were coated on silicon substrates and then irradiated by a pulsed Nd:yttrium-aluminum-garnet laser (λ=532 nm) with various fluences in argon gas atmosphere. Significant changes in microstructures and chemical bonding (sp3/sp2) during laser treatment were investigated by Raman spectroscopy. At a laser fluence below 50 mJ/cm2, the Raman spectrum of the film was similar to that of the original polymer film. In a fluence range from 100 to 650 mJ/cm2, the thermal decomposition of the polymer occurred, resulting in upshift of G peak and downshift of the D peak both with narrower peak width. With increasing laser fluence from 650 to 950 mJ/cm2, both the G and D peaks downshifted simultaneously due to the thermal decomposition. The simultaneous downshift of both peaks indicated the increased sp3/sp2 ratio in the carbon film converted from the polymer. With increasing laser fluence in this range, the thermal decomposition also induced the narrowing of both peaks. The narrowing of both peaks indicated the increased ordering of sp3 and sp2 bonding components in the converted carbon film. The scanning electron microscopy studies provided the further evidence. The carbon films converted from the polymer films may contain the highest sp3 carbon bonding at laser fluences in the range from 850 to 1000 mJ/cm2.

Original languageEnglish (US)
Pages (from-to)945-951
Number of pages7
JournalJournal of Applied Physics
Volume87
Issue number2
DOIs
StatePublished - Jan 15 2000

Fingerprint

Raman spectroscopy
fluence
irradiation
polymers
lasers
thermal decomposition
carbon
yttrium-aluminum garnet
argon
Raman spectra
atmospheres
microstructure
scanning electron microscopy
silicon
gases

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Raman spectroscopy of phenylcarbyne polymer films under pulsed green laser irradiation. / Lu, Y. F.; Huang, S. M.; Sun, Z.

In: Journal of Applied Physics, Vol. 87, No. 2, 15.01.2000, p. 945-951.

Research output: Contribution to journalArticle

@article{d80e9967855846629fa7f262c7cad73a,
title = "Raman spectroscopy of phenylcarbyne polymer films under pulsed green laser irradiation",
abstract = "The polycarbyne polymer films were coated on silicon substrates and then irradiated by a pulsed Nd:yttrium-aluminum-garnet laser (λ=532 nm) with various fluences in argon gas atmosphere. Significant changes in microstructures and chemical bonding (sp3/sp2) during laser treatment were investigated by Raman spectroscopy. At a laser fluence below 50 mJ/cm2, the Raman spectrum of the film was similar to that of the original polymer film. In a fluence range from 100 to 650 mJ/cm2, the thermal decomposition of the polymer occurred, resulting in upshift of G peak and downshift of the D peak both with narrower peak width. With increasing laser fluence from 650 to 950 mJ/cm2, both the G and D peaks downshifted simultaneously due to the thermal decomposition. The simultaneous downshift of both peaks indicated the increased sp3/sp2 ratio in the carbon film converted from the polymer. With increasing laser fluence in this range, the thermal decomposition also induced the narrowing of both peaks. The narrowing of both peaks indicated the increased ordering of sp3 and sp2 bonding components in the converted carbon film. The scanning electron microscopy studies provided the further evidence. The carbon films converted from the polymer films may contain the highest sp3 carbon bonding at laser fluences in the range from 850 to 1000 mJ/cm2.",
author = "Lu, {Y. F.} and Huang, {S. M.} and Z. Sun",
year = "2000",
month = "1",
day = "15",
doi = "10.1063/1.371964",
language = "English (US)",
volume = "87",
pages = "945--951",
journal = "Journal of Applied Physics",
issn = "0021-8979",
publisher = "American Institute of Physics Publising LLC",
number = "2",

}

TY - JOUR

T1 - Raman spectroscopy of phenylcarbyne polymer films under pulsed green laser irradiation

AU - Lu, Y. F.

AU - Huang, S. M.

AU - Sun, Z.

PY - 2000/1/15

Y1 - 2000/1/15

N2 - The polycarbyne polymer films were coated on silicon substrates and then irradiated by a pulsed Nd:yttrium-aluminum-garnet laser (λ=532 nm) with various fluences in argon gas atmosphere. Significant changes in microstructures and chemical bonding (sp3/sp2) during laser treatment were investigated by Raman spectroscopy. At a laser fluence below 50 mJ/cm2, the Raman spectrum of the film was similar to that of the original polymer film. In a fluence range from 100 to 650 mJ/cm2, the thermal decomposition of the polymer occurred, resulting in upshift of G peak and downshift of the D peak both with narrower peak width. With increasing laser fluence from 650 to 950 mJ/cm2, both the G and D peaks downshifted simultaneously due to the thermal decomposition. The simultaneous downshift of both peaks indicated the increased sp3/sp2 ratio in the carbon film converted from the polymer. With increasing laser fluence in this range, the thermal decomposition also induced the narrowing of both peaks. The narrowing of both peaks indicated the increased ordering of sp3 and sp2 bonding components in the converted carbon film. The scanning electron microscopy studies provided the further evidence. The carbon films converted from the polymer films may contain the highest sp3 carbon bonding at laser fluences in the range from 850 to 1000 mJ/cm2.

AB - The polycarbyne polymer films were coated on silicon substrates and then irradiated by a pulsed Nd:yttrium-aluminum-garnet laser (λ=532 nm) with various fluences in argon gas atmosphere. Significant changes in microstructures and chemical bonding (sp3/sp2) during laser treatment were investigated by Raman spectroscopy. At a laser fluence below 50 mJ/cm2, the Raman spectrum of the film was similar to that of the original polymer film. In a fluence range from 100 to 650 mJ/cm2, the thermal decomposition of the polymer occurred, resulting in upshift of G peak and downshift of the D peak both with narrower peak width. With increasing laser fluence from 650 to 950 mJ/cm2, both the G and D peaks downshifted simultaneously due to the thermal decomposition. The simultaneous downshift of both peaks indicated the increased sp3/sp2 ratio in the carbon film converted from the polymer. With increasing laser fluence in this range, the thermal decomposition also induced the narrowing of both peaks. The narrowing of both peaks indicated the increased ordering of sp3 and sp2 bonding components in the converted carbon film. The scanning electron microscopy studies provided the further evidence. The carbon films converted from the polymer films may contain the highest sp3 carbon bonding at laser fluences in the range from 850 to 1000 mJ/cm2.

UR - http://www.scopus.com/inward/record.url?scp=0010559728&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0010559728&partnerID=8YFLogxK

U2 - 10.1063/1.371964

DO - 10.1063/1.371964

M3 - Article

AN - SCOPUS:0010559728

VL - 87

SP - 945

EP - 951

JO - Journal of Applied Physics

JF - Journal of Applied Physics

SN - 0021-8979

IS - 2

ER -