Influence of duration of phosphoric acid pre-etching on bond durability of universal adhesives and surface free-energy characteristics of enamel

Akimasa Tsujimoto, Wayne W. Barkmeier, Toshiki Takamizawa, Hidehiko Watanabe, William W. Johnson, Mark A. Latta, Masashi Miyazaki

Research output: Contribution to journalArticle

13 Citations (Scopus)

Abstract

The purpose of this study was to evaluate the influence of duration of phosphoric acid pre-etching on the bond durability of universal adhesives and the surface free-energy characteristics of enamel. Three universal adhesives and extracted human molars were used. Two no-pre-etching groups were prepared: ground enamel; and enamel after ultrasonic cleaning with distilled water for 30 s to remove the smear layer. Four pre-etching groups were prepared: enamel pre-etched with phosphoric acid for 3, 5, 10, and 15 s. Shear bond strength (SBS) values of universal adhesive after no thermal cycling and after 30,000 or 60,000 thermal cycles, and surface free-energy values of enamel surfaces, calculated from contact angle measurements, were determined. The specimens that had been pre-etched showed significantly higher SBS and surface free-energy values than the specimens that had not been pre-etched, regardless of the aging condition and adhesive type. The SBS and surface free-energy values did not increase for pre-etching times of longer than 3 s. There were no significant differences in SBS values and surface free-energy characteristics between the specimens with and without a smear layer. The results of this study suggest that phosphoric acid pre-etching of enamel improves the bond durability of universal adhesives and the surface free-energy characteristics of enamel, but these bonding properties do not increase for phosphoric acid pre-etching times of longer than 3 s.

Original languageEnglish (US)
Pages (from-to)377-386
Number of pages10
JournalEuropean Journal of Oral Sciences
Volume124
Issue number4
DOIs
StatePublished - Aug 1 2016

Fingerprint

Dental Enamel
Adhesives
Shear Strength
Smear Layer
Hot Temperature
phosphoric acid
Ultrasonics
Water

Keywords

  • bond durability
  • phosphoric acid pre-etching
  • surface free-energy
  • universal adhesive

ASJC Scopus subject areas

  • Dentistry(all)

Cite this

Influence of duration of phosphoric acid pre-etching on bond durability of universal adhesives and surface free-energy characteristics of enamel. / Tsujimoto, Akimasa; Barkmeier, Wayne W.; Takamizawa, Toshiki; Watanabe, Hidehiko; Johnson, William W.; Latta, Mark A.; Miyazaki, Masashi.

In: European Journal of Oral Sciences, Vol. 124, No. 4, 01.08.2016, p. 377-386.

Research output: Contribution to journalArticle

Tsujimoto, Akimasa ; Barkmeier, Wayne W. ; Takamizawa, Toshiki ; Watanabe, Hidehiko ; Johnson, William W. ; Latta, Mark A. ; Miyazaki, Masashi. / Influence of duration of phosphoric acid pre-etching on bond durability of universal adhesives and surface free-energy characteristics of enamel. In: European Journal of Oral Sciences. 2016 ; Vol. 124, No. 4. pp. 377-386.
@article{b0e45940c7a04f1b99a78dcf62016c68,
title = "Influence of duration of phosphoric acid pre-etching on bond durability of universal adhesives and surface free-energy characteristics of enamel",
abstract = "The purpose of this study was to evaluate the influence of duration of phosphoric acid pre-etching on the bond durability of universal adhesives and the surface free-energy characteristics of enamel. Three universal adhesives and extracted human molars were used. Two no-pre-etching groups were prepared: ground enamel; and enamel after ultrasonic cleaning with distilled water for 30 s to remove the smear layer. Four pre-etching groups were prepared: enamel pre-etched with phosphoric acid for 3, 5, 10, and 15 s. Shear bond strength (SBS) values of universal adhesive after no thermal cycling and after 30,000 or 60,000 thermal cycles, and surface free-energy values of enamel surfaces, calculated from contact angle measurements, were determined. The specimens that had been pre-etched showed significantly higher SBS and surface free-energy values than the specimens that had not been pre-etched, regardless of the aging condition and adhesive type. The SBS and surface free-energy values did not increase for pre-etching times of longer than 3 s. There were no significant differences in SBS values and surface free-energy characteristics between the specimens with and without a smear layer. The results of this study suggest that phosphoric acid pre-etching of enamel improves the bond durability of universal adhesives and the surface free-energy characteristics of enamel, but these bonding properties do not increase for phosphoric acid pre-etching times of longer than 3 s.",
keywords = "bond durability, phosphoric acid pre-etching, surface free-energy, universal adhesive",
author = "Akimasa Tsujimoto and Barkmeier, {Wayne W.} and Toshiki Takamizawa and Hidehiko Watanabe and Johnson, {William W.} and Latta, {Mark A.} and Masashi Miyazaki",
year = "2016",
month = "8",
day = "1",
doi = "10.1111/eos.12284",
language = "English (US)",
volume = "124",
pages = "377--386",
journal = "European Journal of Oral Sciences",
issn = "0909-8836",
publisher = "Blackwell Munksgaard",
number = "4",

}

TY - JOUR

T1 - Influence of duration of phosphoric acid pre-etching on bond durability of universal adhesives and surface free-energy characteristics of enamel

AU - Tsujimoto, Akimasa

AU - Barkmeier, Wayne W.

AU - Takamizawa, Toshiki

AU - Watanabe, Hidehiko

AU - Johnson, William W.

AU - Latta, Mark A.

AU - Miyazaki, Masashi

PY - 2016/8/1

Y1 - 2016/8/1

N2 - The purpose of this study was to evaluate the influence of duration of phosphoric acid pre-etching on the bond durability of universal adhesives and the surface free-energy characteristics of enamel. Three universal adhesives and extracted human molars were used. Two no-pre-etching groups were prepared: ground enamel; and enamel after ultrasonic cleaning with distilled water for 30 s to remove the smear layer. Four pre-etching groups were prepared: enamel pre-etched with phosphoric acid for 3, 5, 10, and 15 s. Shear bond strength (SBS) values of universal adhesive after no thermal cycling and after 30,000 or 60,000 thermal cycles, and surface free-energy values of enamel surfaces, calculated from contact angle measurements, were determined. The specimens that had been pre-etched showed significantly higher SBS and surface free-energy values than the specimens that had not been pre-etched, regardless of the aging condition and adhesive type. The SBS and surface free-energy values did not increase for pre-etching times of longer than 3 s. There were no significant differences in SBS values and surface free-energy characteristics between the specimens with and without a smear layer. The results of this study suggest that phosphoric acid pre-etching of enamel improves the bond durability of universal adhesives and the surface free-energy characteristics of enamel, but these bonding properties do not increase for phosphoric acid pre-etching times of longer than 3 s.

AB - The purpose of this study was to evaluate the influence of duration of phosphoric acid pre-etching on the bond durability of universal adhesives and the surface free-energy characteristics of enamel. Three universal adhesives and extracted human molars were used. Two no-pre-etching groups were prepared: ground enamel; and enamel after ultrasonic cleaning with distilled water for 30 s to remove the smear layer. Four pre-etching groups were prepared: enamel pre-etched with phosphoric acid for 3, 5, 10, and 15 s. Shear bond strength (SBS) values of universal adhesive after no thermal cycling and after 30,000 or 60,000 thermal cycles, and surface free-energy values of enamel surfaces, calculated from contact angle measurements, were determined. The specimens that had been pre-etched showed significantly higher SBS and surface free-energy values than the specimens that had not been pre-etched, regardless of the aging condition and adhesive type. The SBS and surface free-energy values did not increase for pre-etching times of longer than 3 s. There were no significant differences in SBS values and surface free-energy characteristics between the specimens with and without a smear layer. The results of this study suggest that phosphoric acid pre-etching of enamel improves the bond durability of universal adhesives and the surface free-energy characteristics of enamel, but these bonding properties do not increase for phosphoric acid pre-etching times of longer than 3 s.

KW - bond durability

KW - phosphoric acid pre-etching

KW - surface free-energy

KW - universal adhesive

UR - http://www.scopus.com/inward/record.url?scp=84977646831&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84977646831&partnerID=8YFLogxK

U2 - 10.1111/eos.12284

DO - 10.1111/eos.12284

M3 - Article

C2 - 27315775

AN - SCOPUS:84977646831

VL - 124

SP - 377

EP - 386

JO - European Journal of Oral Sciences

JF - European Journal of Oral Sciences

SN - 0909-8836

IS - 4

ER -