Deconvolution of the Co3O4 (110) Fuchs-Kliewer phonon spectrum

E. M. Marsh, S. C. Petitto, G. S. Harbison, K. W. Wulser, M. A. Langell

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

The Fuchs-Kliewer phonon spectrum of single crystal Co3O4 (110) has been treated with a Fourier transform log deconvolution method, which removes multiple scattering features from the single loss spectrum. Auger electron spectroscopy (AES), x-ray photoelectron spectroscopy (XPS) and low-energy electron diffraction (LEED) were first used to characterize the Co3O4 crystal establishing the cleanliness, composition, and order of the (110) surface. High resolution electron energy loss spectroscopy (HREELS) was then used to obtain the phonon spectrum for an incident electron energy of 3.77 eV. Due to the strong dipole cross section for the Fuchs-Kliewer phonon modes, intense multiple electron scattering was detected, which provided a complicated and overlapping combination of all possible loss modes. Deconvolution removed the multiple loss modes to produce well-resolved Fuchs-Kliewer fundamental phonon losses at 218, 373, 598, and 682 cm-1 (27.0, 46.2, 74.1, and 84.6 meV). These values are compared to the fundamental loss energies obtained by resolving the overlapping peak structure with standard peak fitting procedures, which confirmed the single loss energies obtained with the deconvolution procedure. Deconvolution results from the four fundamental phonon spectrum of single crystal Co3O4 (110) were also compared to those from the simpler spectra of CoO(100) and thin-film CoO(100)- Co3O4 epitaxy and some practical aspects of the deconvolution process discussed in this context.

Original languageEnglish (US)
Pages (from-to)1061-1066
Number of pages6
JournalJournal of Vacuum Science and Technology A: Vacuum, Surfaces and Films
Volume23
Issue number4
DOIs
StatePublished - Jul 1 2005

Fingerprint

Deconvolution
energy dissipation
Multiple scattering
Energy dissipation
Single crystals
electron energy
cleanliness
Electron scattering
Low energy electron diffraction
Electron energy loss spectroscopy
single crystals
Auger electron spectroscopy
Photoelectron spectroscopy
Epitaxial growth
epitaxy
x ray spectroscopy
Auger spectroscopy
electron spectroscopy
Fourier transforms
electron scattering

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

Cite this

Deconvolution of the Co3O4 (110) Fuchs-Kliewer phonon spectrum. / Marsh, E. M.; Petitto, S. C.; Harbison, G. S.; Wulser, K. W.; Langell, M. A.

In: Journal of Vacuum Science and Technology A: Vacuum, Surfaces and Films, Vol. 23, No. 4, 01.07.2005, p. 1061-1066.

Research output: Contribution to journalArticle

Marsh, E. M. ; Petitto, S. C. ; Harbison, G. S. ; Wulser, K. W. ; Langell, M. A. / Deconvolution of the Co3O4 (110) Fuchs-Kliewer phonon spectrum. In: Journal of Vacuum Science and Technology A: Vacuum, Surfaces and Films. 2005 ; Vol. 23, No. 4. pp. 1061-1066.
@article{49955257c1b24abc83acd60bab7d1b90,
title = "Deconvolution of the Co3O4 (110) Fuchs-Kliewer phonon spectrum",
abstract = "The Fuchs-Kliewer phonon spectrum of single crystal Co3O4 (110) has been treated with a Fourier transform log deconvolution method, which removes multiple scattering features from the single loss spectrum. Auger electron spectroscopy (AES), x-ray photoelectron spectroscopy (XPS) and low-energy electron diffraction (LEED) were first used to characterize the Co3O4 crystal establishing the cleanliness, composition, and order of the (110) surface. High resolution electron energy loss spectroscopy (HREELS) was then used to obtain the phonon spectrum for an incident electron energy of 3.77 eV. Due to the strong dipole cross section for the Fuchs-Kliewer phonon modes, intense multiple electron scattering was detected, which provided a complicated and overlapping combination of all possible loss modes. Deconvolution removed the multiple loss modes to produce well-resolved Fuchs-Kliewer fundamental phonon losses at 218, 373, 598, and 682 cm-1 (27.0, 46.2, 74.1, and 84.6 meV). These values are compared to the fundamental loss energies obtained by resolving the overlapping peak structure with standard peak fitting procedures, which confirmed the single loss energies obtained with the deconvolution procedure. Deconvolution results from the four fundamental phonon spectrum of single crystal Co3O4 (110) were also compared to those from the simpler spectra of CoO(100) and thin-film CoO(100)- Co3O4 epitaxy and some practical aspects of the deconvolution process discussed in this context.",
author = "Marsh, {E. M.} and Petitto, {S. C.} and Harbison, {G. S.} and Wulser, {K. W.} and Langell, {M. A.}",
year = "2005",
month = "7",
day = "1",
doi = "10.1116/1.1863972",
language = "English (US)",
volume = "23",
pages = "1061--1066",
journal = "Journal of Vacuum Science and Technology A",
issn = "0734-2101",
publisher = "AVS Science and Technology Society",
number = "4",

}

TY - JOUR

T1 - Deconvolution of the Co3O4 (110) Fuchs-Kliewer phonon spectrum

AU - Marsh, E. M.

AU - Petitto, S. C.

AU - Harbison, G. S.

AU - Wulser, K. W.

AU - Langell, M. A.

PY - 2005/7/1

Y1 - 2005/7/1

N2 - The Fuchs-Kliewer phonon spectrum of single crystal Co3O4 (110) has been treated with a Fourier transform log deconvolution method, which removes multiple scattering features from the single loss spectrum. Auger electron spectroscopy (AES), x-ray photoelectron spectroscopy (XPS) and low-energy electron diffraction (LEED) were first used to characterize the Co3O4 crystal establishing the cleanliness, composition, and order of the (110) surface. High resolution electron energy loss spectroscopy (HREELS) was then used to obtain the phonon spectrum for an incident electron energy of 3.77 eV. Due to the strong dipole cross section for the Fuchs-Kliewer phonon modes, intense multiple electron scattering was detected, which provided a complicated and overlapping combination of all possible loss modes. Deconvolution removed the multiple loss modes to produce well-resolved Fuchs-Kliewer fundamental phonon losses at 218, 373, 598, and 682 cm-1 (27.0, 46.2, 74.1, and 84.6 meV). These values are compared to the fundamental loss energies obtained by resolving the overlapping peak structure with standard peak fitting procedures, which confirmed the single loss energies obtained with the deconvolution procedure. Deconvolution results from the four fundamental phonon spectrum of single crystal Co3O4 (110) were also compared to those from the simpler spectra of CoO(100) and thin-film CoO(100)- Co3O4 epitaxy and some practical aspects of the deconvolution process discussed in this context.

AB - The Fuchs-Kliewer phonon spectrum of single crystal Co3O4 (110) has been treated with a Fourier transform log deconvolution method, which removes multiple scattering features from the single loss spectrum. Auger electron spectroscopy (AES), x-ray photoelectron spectroscopy (XPS) and low-energy electron diffraction (LEED) were first used to characterize the Co3O4 crystal establishing the cleanliness, composition, and order of the (110) surface. High resolution electron energy loss spectroscopy (HREELS) was then used to obtain the phonon spectrum for an incident electron energy of 3.77 eV. Due to the strong dipole cross section for the Fuchs-Kliewer phonon modes, intense multiple electron scattering was detected, which provided a complicated and overlapping combination of all possible loss modes. Deconvolution removed the multiple loss modes to produce well-resolved Fuchs-Kliewer fundamental phonon losses at 218, 373, 598, and 682 cm-1 (27.0, 46.2, 74.1, and 84.6 meV). These values are compared to the fundamental loss energies obtained by resolving the overlapping peak structure with standard peak fitting procedures, which confirmed the single loss energies obtained with the deconvolution procedure. Deconvolution results from the four fundamental phonon spectrum of single crystal Co3O4 (110) were also compared to those from the simpler spectra of CoO(100) and thin-film CoO(100)- Co3O4 epitaxy and some practical aspects of the deconvolution process discussed in this context.

UR - http://www.scopus.com/inward/record.url?scp=31044453166&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=31044453166&partnerID=8YFLogxK

U2 - 10.1116/1.1863972

DO - 10.1116/1.1863972

M3 - Article

AN - SCOPUS:31044453166

VL - 23

SP - 1061

EP - 1066

JO - Journal of Vacuum Science and Technology A

JF - Journal of Vacuum Science and Technology A

SN - 0734-2101

IS - 4

ER -