Characterization of crack growth rate of sulfur-extended asphalt mixtures using cyclic semicircular bending test

Jun Zhang, Maryam Sakhaeifar, Dallas N. Little, Amit Bhasin, Yong Rak Kim

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

Characterizing crack propagation of asphalt mixtures is helpful for optimizing mixture design and predicting cracking performance of asphalt pavements. This paper explores a new method based on the cyclic semicircular bending (SCB) test to characterize crack growth rate and evaluate fatigue cracking resistance of asphalt mixtures. For characterizing crack growth rate, the difficulty is the measurement of crack length during testing. A digital image correlation (DIC) was used to track the crack propagation during the test, which was used to establish a correlation curve with the corresponding crack mouth opening displacement (CMOD) measurements. Four sulfur-extended asphalt (SEA) mixtures with different dosages of sulfur were evaluated with the proposed cyclic SCB test. The results of the test fitted well to the Paris law function, and the Paris law coefficients of SEA mixtures were identified. They were also consistent with the test results from the monotonic SCB test and horizontal strain field of the crack tip characterized using the DIC. The cyclic SCB test showed substantially lower coefficients of variance in terms of the number of cycles to failure compared with other traditional fatigue tests such as the bending beam fatigue test and the Texas overlay test. Regarding the effects of sulfur, test results showed that a low level of sulfur addition, such as 15%, softens asphalt binder to the stage where more damage can be induced in a controlled-stress mode of loading, while extra sulfur would act as fillers to stiffen the asphalt binder when the dosage was greater, such as 30%-45%.

Original languageEnglish (US)
Article number04018311
JournalJournal of Materials in Civil Engineering
Volume30
Issue number12
DOIs
StatePublished - Dec 1 2018

Fingerprint

Asphalt mixtures
Bending tests
Sulfur
Crack propagation
asphalt
Fatigue of materials
Asphalt
Binders
Cracks
Displacement measurement
Bending (deformation)
Asphalt pavements
Crack tips
Fillers
Testing

Keywords

  • Asphalt mixtures
  • Cyclic semicircular bending test
  • Digital image correlation
  • Fatigue cracking
  • Paris law
  • Sulfur-extended asphalt

ASJC Scopus subject areas

  • Civil and Structural Engineering
  • Building and Construction
  • Materials Science(all)
  • Mechanics of Materials

Cite this

Characterization of crack growth rate of sulfur-extended asphalt mixtures using cyclic semicircular bending test. / Zhang, Jun; Sakhaeifar, Maryam; Little, Dallas N.; Bhasin, Amit; Kim, Yong Rak.

In: Journal of Materials in Civil Engineering, Vol. 30, No. 12, 04018311, 01.12.2018.

Research output: Contribution to journalArticle

@article{f9e8f4da2a484f9d9ee9ac34b8d87d39,
title = "Characterization of crack growth rate of sulfur-extended asphalt mixtures using cyclic semicircular bending test",
abstract = "Characterizing crack propagation of asphalt mixtures is helpful for optimizing mixture design and predicting cracking performance of asphalt pavements. This paper explores a new method based on the cyclic semicircular bending (SCB) test to characterize crack growth rate and evaluate fatigue cracking resistance of asphalt mixtures. For characterizing crack growth rate, the difficulty is the measurement of crack length during testing. A digital image correlation (DIC) was used to track the crack propagation during the test, which was used to establish a correlation curve with the corresponding crack mouth opening displacement (CMOD) measurements. Four sulfur-extended asphalt (SEA) mixtures with different dosages of sulfur were evaluated with the proposed cyclic SCB test. The results of the test fitted well to the Paris law function, and the Paris law coefficients of SEA mixtures were identified. They were also consistent with the test results from the monotonic SCB test and horizontal strain field of the crack tip characterized using the DIC. The cyclic SCB test showed substantially lower coefficients of variance in terms of the number of cycles to failure compared with other traditional fatigue tests such as the bending beam fatigue test and the Texas overlay test. Regarding the effects of sulfur, test results showed that a low level of sulfur addition, such as 15{\%}, softens asphalt binder to the stage where more damage can be induced in a controlled-stress mode of loading, while extra sulfur would act as fillers to stiffen the asphalt binder when the dosage was greater, such as 30{\%}-45{\%}.",
keywords = "Asphalt mixtures, Cyclic semicircular bending test, Digital image correlation, Fatigue cracking, Paris law, Sulfur-extended asphalt",
author = "Jun Zhang and Maryam Sakhaeifar and Little, {Dallas N.} and Amit Bhasin and Kim, {Yong Rak}",
year = "2018",
month = "12",
day = "1",
doi = "10.1061/(ASCE)MT.1943-5533.0002517",
language = "English (US)",
volume = "30",
journal = "Journal of Materials in Civil Engineering",
issn = "0899-1561",
publisher = "American Society of Civil Engineers (ASCE)",
number = "12",

}

TY - JOUR

T1 - Characterization of crack growth rate of sulfur-extended asphalt mixtures using cyclic semicircular bending test

AU - Zhang, Jun

AU - Sakhaeifar, Maryam

AU - Little, Dallas N.

AU - Bhasin, Amit

AU - Kim, Yong Rak

PY - 2018/12/1

Y1 - 2018/12/1

N2 - Characterizing crack propagation of asphalt mixtures is helpful for optimizing mixture design and predicting cracking performance of asphalt pavements. This paper explores a new method based on the cyclic semicircular bending (SCB) test to characterize crack growth rate and evaluate fatigue cracking resistance of asphalt mixtures. For characterizing crack growth rate, the difficulty is the measurement of crack length during testing. A digital image correlation (DIC) was used to track the crack propagation during the test, which was used to establish a correlation curve with the corresponding crack mouth opening displacement (CMOD) measurements. Four sulfur-extended asphalt (SEA) mixtures with different dosages of sulfur were evaluated with the proposed cyclic SCB test. The results of the test fitted well to the Paris law function, and the Paris law coefficients of SEA mixtures were identified. They were also consistent with the test results from the monotonic SCB test and horizontal strain field of the crack tip characterized using the DIC. The cyclic SCB test showed substantially lower coefficients of variance in terms of the number of cycles to failure compared with other traditional fatigue tests such as the bending beam fatigue test and the Texas overlay test. Regarding the effects of sulfur, test results showed that a low level of sulfur addition, such as 15%, softens asphalt binder to the stage where more damage can be induced in a controlled-stress mode of loading, while extra sulfur would act as fillers to stiffen the asphalt binder when the dosage was greater, such as 30%-45%.

AB - Characterizing crack propagation of asphalt mixtures is helpful for optimizing mixture design and predicting cracking performance of asphalt pavements. This paper explores a new method based on the cyclic semicircular bending (SCB) test to characterize crack growth rate and evaluate fatigue cracking resistance of asphalt mixtures. For characterizing crack growth rate, the difficulty is the measurement of crack length during testing. A digital image correlation (DIC) was used to track the crack propagation during the test, which was used to establish a correlation curve with the corresponding crack mouth opening displacement (CMOD) measurements. Four sulfur-extended asphalt (SEA) mixtures with different dosages of sulfur were evaluated with the proposed cyclic SCB test. The results of the test fitted well to the Paris law function, and the Paris law coefficients of SEA mixtures were identified. They were also consistent with the test results from the monotonic SCB test and horizontal strain field of the crack tip characterized using the DIC. The cyclic SCB test showed substantially lower coefficients of variance in terms of the number of cycles to failure compared with other traditional fatigue tests such as the bending beam fatigue test and the Texas overlay test. Regarding the effects of sulfur, test results showed that a low level of sulfur addition, such as 15%, softens asphalt binder to the stage where more damage can be induced in a controlled-stress mode of loading, while extra sulfur would act as fillers to stiffen the asphalt binder when the dosage was greater, such as 30%-45%.

KW - Asphalt mixtures

KW - Cyclic semicircular bending test

KW - Digital image correlation

KW - Fatigue cracking

KW - Paris law

KW - Sulfur-extended asphalt

UR - http://www.scopus.com/inward/record.url?scp=85053689865&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85053689865&partnerID=8YFLogxK

U2 - 10.1061/(ASCE)MT.1943-5533.0002517

DO - 10.1061/(ASCE)MT.1943-5533.0002517

M3 - Article

AN - SCOPUS:85053689865

VL - 30

JO - Journal of Materials in Civil Engineering

JF - Journal of Materials in Civil Engineering

SN - 0899-1561

IS - 12

M1 - 04018311

ER -