Bubble Removal in Rotational Molding

Research output: Contribution to journalArticle

33 Citations (Scopus)

Abstract

Closed form solutions have been obtained for bubble dissolution in typical polymer melts encountered in rotational molding. The solutions are in excellent agreement with experimental data available in the literature. Using these solutions, it is shown that under typical rotational molding conditions the polymer melts may be almost saturated. As a result, bubble shrinkage occurs over long periods. Depending on the degree of saturation, surface tension may contribute substantially to the concentration gradient that drives bubble shrinkage. It is also shown that a pressure increase imposed on a nearly saturated polymer melt leads to a steep concentration gradient at the bubble/melt interface that can cause extremely fast bubble shrinkage. Applied to the rotational molding process, such a pressure increase can result in substantial cycle-time shortening through elimination (or reduction) of the currently used excessive heating. A further benefit may be that additional resins, which at present cannot be used because of oxidation at sustained high-temperatures, can become available to the rotational molding industry. Under the under-saturated conditions created by a pressure increase, the effect of surface tension on the rate of bubble shrinkage is negligible.

Original languageEnglish (US)
Pages (from-to)388-394
Number of pages7
JournalPolymer Engineering and Science
Volume44
Issue number2
DOIs
StatePublished - Feb 1 2004

Fingerprint

Rotational molding
Bubbles (in fluids)
Polymer melts
Surface tension
Dissolution
Resins
Heating
Oxidation
Industry
Temperature

ASJC Scopus subject areas

  • Chemistry(all)
  • Polymers and Plastics
  • Materials Chemistry

Cite this

Bubble Removal in Rotational Molding. / Gogos, George.

In: Polymer Engineering and Science, Vol. 44, No. 2, 01.02.2004, p. 388-394.

Research output: Contribution to journalArticle

@article{db5c5483ba254ac2b7610b2710180c7c,
title = "Bubble Removal in Rotational Molding",
abstract = "Closed form solutions have been obtained for bubble dissolution in typical polymer melts encountered in rotational molding. The solutions are in excellent agreement with experimental data available in the literature. Using these solutions, it is shown that under typical rotational molding conditions the polymer melts may be almost saturated. As a result, bubble shrinkage occurs over long periods. Depending on the degree of saturation, surface tension may contribute substantially to the concentration gradient that drives bubble shrinkage. It is also shown that a pressure increase imposed on a nearly saturated polymer melt leads to a steep concentration gradient at the bubble/melt interface that can cause extremely fast bubble shrinkage. Applied to the rotational molding process, such a pressure increase can result in substantial cycle-time shortening through elimination (or reduction) of the currently used excessive heating. A further benefit may be that additional resins, which at present cannot be used because of oxidation at sustained high-temperatures, can become available to the rotational molding industry. Under the under-saturated conditions created by a pressure increase, the effect of surface tension on the rate of bubble shrinkage is negligible.",
author = "George Gogos",
year = "2004",
month = "2",
day = "1",
doi = "10.1002/pen.20035",
language = "English (US)",
volume = "44",
pages = "388--394",
journal = "Polymer Engineering and Science",
issn = "0032-3888",
publisher = "John Wiley and Sons Inc.",
number = "2",

}

TY - JOUR

T1 - Bubble Removal in Rotational Molding

AU - Gogos, George

PY - 2004/2/1

Y1 - 2004/2/1

N2 - Closed form solutions have been obtained for bubble dissolution in typical polymer melts encountered in rotational molding. The solutions are in excellent agreement with experimental data available in the literature. Using these solutions, it is shown that under typical rotational molding conditions the polymer melts may be almost saturated. As a result, bubble shrinkage occurs over long periods. Depending on the degree of saturation, surface tension may contribute substantially to the concentration gradient that drives bubble shrinkage. It is also shown that a pressure increase imposed on a nearly saturated polymer melt leads to a steep concentration gradient at the bubble/melt interface that can cause extremely fast bubble shrinkage. Applied to the rotational molding process, such a pressure increase can result in substantial cycle-time shortening through elimination (or reduction) of the currently used excessive heating. A further benefit may be that additional resins, which at present cannot be used because of oxidation at sustained high-temperatures, can become available to the rotational molding industry. Under the under-saturated conditions created by a pressure increase, the effect of surface tension on the rate of bubble shrinkage is negligible.

AB - Closed form solutions have been obtained for bubble dissolution in typical polymer melts encountered in rotational molding. The solutions are in excellent agreement with experimental data available in the literature. Using these solutions, it is shown that under typical rotational molding conditions the polymer melts may be almost saturated. As a result, bubble shrinkage occurs over long periods. Depending on the degree of saturation, surface tension may contribute substantially to the concentration gradient that drives bubble shrinkage. It is also shown that a pressure increase imposed on a nearly saturated polymer melt leads to a steep concentration gradient at the bubble/melt interface that can cause extremely fast bubble shrinkage. Applied to the rotational molding process, such a pressure increase can result in substantial cycle-time shortening through elimination (or reduction) of the currently used excessive heating. A further benefit may be that additional resins, which at present cannot be used because of oxidation at sustained high-temperatures, can become available to the rotational molding industry. Under the under-saturated conditions created by a pressure increase, the effect of surface tension on the rate of bubble shrinkage is negligible.

UR - http://www.scopus.com/inward/record.url?scp=1842816574&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=1842816574&partnerID=8YFLogxK

U2 - 10.1002/pen.20035

DO - 10.1002/pen.20035

M3 - Article

VL - 44

SP - 388

EP - 394

JO - Polymer Engineering and Science

JF - Polymer Engineering and Science

SN - 0032-3888

IS - 2

ER -